BA-8010 High Adhesive and Cohesive Strength PAA Binder for Graphite-based Anode
A Water-based Polyacrylate Binder for Effectively Suppressing Electrode Expansion and Efficiently Improving Cell Durability
Advantages:
- Small Resilience after Compact
- Low Internal Impedance Available
- Good Performance at Low Temperature and Excellent Cyclability
- Safe, Environmental and Friendly to Industrial Sites and Operators
- Excellent Electrolyte Resistance Capability with Low Swelling
- Excellent Electrochemical Stability and Thermal Stability
- Excellent Mechanical-processing Stability
| ITEM | BA-8010 | |
| Appearance | Milky-white and Light-yellow Liquid | |
| D50(um) | 3-5μm | |
| Solid Content（150℃×30min） | 15±0.2% | |
| pH | 7-9 | |
| Viscosity（12rpm/30℃） | ＞25000mPa.S | |
| Tg, °C（DSC Method） | 115℃ | |
| Decomposition | ＞270℃ | |
| Stability After Dispersing | No Demulsification (Grinding/Calcium/Freeze-thaw Testing) | |
| Adhesion& Cohension Generated for Electrodes | High （Rolling Test at ф3mm Cylinder） | |
| Application | Graphite Anode | |
- Use directly or use after diluting
- The properties of adhesion will not be affected when stirring at high speed with powder materials in the kettle
- The adhesion property of the slurry should be controlled by adjusting the quantity of water requested by the process specification
- Sifting, defoaming and discharging materials when the requested fineness is available after dispersion
- Store the products in the temperature of 15 ~ 30 ℃, in case of frozen, just unfreeze and mixing for a normal use
- One-year Warranty
- Non-dangerous goods, transportation as general chemicals
- 50KG or 200KG per Barrel